Hygroscopic Mg–Al LDHs composite microspheres for highly efficient hyperspectral camouflage in the VIS and NIR wavebands

In order to enhance the hyperspectral camouflage efficacy of stealth coatings against a natural vegetative backdrop, LiCl, known for its significant hygroscopic properties, was incorporated into green Mg–Al layered double hydroxide (Mg–Al LDHs) material. Micron-sized composite microspheres were subsequently synthesized via the spray-drying granulation technique. The structure, morphology, and chemical composition of these microspheres were thoroughly characterized by X-ray diffraction, scanning electron microscopy, laser particle size analysis, nitrogen adsorption–desorption isotherms, and Fourier-transform infrared spectroscopy. The effect of LiCl content on the moisture absorption capacity and near-infrared reflectance spectra of the microspheres was systematically evaluated. We found that incorporating an optimal amount of LiCl into the internal pores of the Mg–Al LDHs microspheres did not compromise their smooth surface morphology and uniform particulate distribution. Notably, when the LiCl content was 10%, the maximum saturation moisture uptake ratio of the coating increased to 0.75 g/g. This hygroscopicity significantly enhanced the absorption and scattering of near-infrared radiation by the coating while concurrently improving its ability to modulate the shape and reflectance of both the visible and near-infrared spectral curves. Spectral congruence between the synthetic coating and natural green foliage was quantified at 97.41%. Moreover, this performance was maintained over 10 cycles of programmed drying and re-humidification, and the coating consistently demonstrated stable hygroscopic properties and sustained over 95% spectral congruence. These optimized artificial coatings were found to effectively confuse hyperspectral classification algorithms, thus blending seamlessly into a natural foliage backdrop. This study provides a new method for regulating VIS and NIR spectral (visible–near infrared spectrum) features, which will be critical for applications in advanced hyperspectral camouflage materials.


Preparation of LiCl-LDHs composite microspheres
The Mg-Al layered double hydroxides (LDHs) were synthesized using a classical co-precipitation method.The synthesis commenced by dissolving 0.3 mol of MgCl 2 and 0.1 mol of AlCl 3 •6H 2 O in 500 ml of deionized water, with continuous magnetic stirring until complete dissolution.Subsequently, a specific volume of dye solution, composed of alizarin green, acidic yellow, and deionized water in a mass ratio of 1:21:40, was added.Following this, a 0.8 M sodium hydroxide solution was incrementally added to the mixture to adjust the pH of the reaction solution to 10.After the reaction concluded, the mixture could age for an additional 4 h, followed by washing with deionized water and drying to yield green Mg-Al LDHs powder.
In the preparation of LiCl-LDHs composite microspheres, 500 g of Mg-Al LDHs powder was dispersed in 4.5 L of deionized water, and subsequently milled to form a slurry with a 10 wt% concentration at a rotational speed of 2000 rpm using a sand mill.During the milling process, an additional x wt% of anhydrous lithium chloride was introduced.Ultimately, composite microspheres with an x% LiCl-LDHs content were produced through a centrifugal spray granulation technique, where the atomization frequency was carefully adjusted to 25 Hz.

Preparation of hyperspectral camouflage coatings
A hyperspectral camouflage coating was developed, incorporating x% of LiCl-LDHs composite microspheres as the functional fillers and using acrylic resin as the binder.Initially, the acrylic resin was mixed with a predetermined amount of diluent, followed by the addition of 0.5 wt% KH560 silane coupling agent and oleic acid.Subsequently, 360 wt% of the microsphere powders and 0.1 wt% of a curing agent were incorporated into the mixture.This blend was then thoroughly dispersed with a homogenizer.Finally, the formulation was applied in an even layer onto the aluminum sheet via an air spraying method and allowed to cure at room temperature for 24 h.

Characterization and measurements
The sample composition and phase structure were characterized using a Bruker D2 X-ray diffractometer, which utilized monochromatic Cu Kα radiation (λ = 0.15406 nm) at settings of 40 kV and 30 mA, featuring a step size of 0.02° and a scanning speed of 5° per minute.The particle size distribution was investigated using an LS-POP (9)  laser particle size analyzer.The sample particle morphology was observed with a FEI QUANTA 250 field emission scanning electron microscope.Adsorption/desorption BET curves were evaluated using a Micromeritics ASAP2460 surface area and porosimetry analyzer.Infrared transmission spectra spanning 4000-400 cm −1 were recorded using a BRUKER Tensor 27 Fourier-transform infrared spectrometer.The reflectance spectra for the powder samples, within the wavelength range of 350-2500 nm, were assessed with a PerkinElmer Lambda 750 UV-VIS-NIR spectrophotometer.
The determination of the water content in composite microsphere powder and coating materials proceeds as described below.Initially, samples are subjected to drying in an oven at 100 °C until they reach constant weight, indicative of the complete removal of moisture and impurities.This weight is designated as m 1 .Subsequently, samples are transferred to a controlled environment chamber set at 20 °C and 99% humidity, where they are left until water absorption equilibrates, at which point the weight, denoted as m 2 , is measured.Utilizing the mass measurements before and after moisture exposure, the saturated adsorptive capacity (Q, expressed in g/g), is calculated using formula (1).
To evaluate the spectral congruity between the sample and the plant leaves, the spectral correlation coefficient, as defined by Eq. ( 2), was utilized.In this context, x i represents the spectral value attributed to the sample, while y i corresponds to the spectral value of the plant leaves.x i and y i denote the respective average spectral values.If the material's spectrum is identical to that of the plant leaves, the correlation coefficient will be 1.Otherwise, the correlation coefficient will register as less than 1 19 .

Results and discussion
Figure 1 presents the XRD analysis of the LiCl-LDHs composite microspheres, revealing the characteristic diffraction peaks of the Mg-Al LDHs in the sample's XRD pattern 20 .Specifically, the peaks near 11° and 23° aligned with the (003) and (006) crystal planes of the Mg-Al LDHs, demonstrating the quintessential peaks of hydrotalcite.Additionally, the absence of diffraction peaks from extraneous substances suggested that LiCl was mechanically intermixed with Mg-Al LDHs in an amorphous state, rather than reacting with them 21 .The incorporation of a suitable quantity of LiCl was found to enhance the crystallinity of the LDHs, achieving optimal crystallinity at a LiCl composition of 10%.However, an increase in LiCl content beyond this point led to a diminished intensity of the Mg-Al LDHs diffraction peaks.The superfluous amorphous LiCl diminished the relative concentration of the Mg-Al LDHs in the composite.Then, the smaller-sized Li + ions possibly infiltrated the lamellar structure of hydrotalcite, thus disturbing the crystal lattice 22 .Figure 2 presents the SEM images of the LiCl-LDHs composite microspheres with different LiCl concentrations, demonstrating that post-spray drying, samples with minimal LiCl content possessed spherical particles characterized by a uniform morphology and smooth exteriors.The particle size exhibited a broad distribution, with the dominance of smaller particles.As the LiCl concentration increased, a marked increase was observed in the larger particles, which was attributed to the spray granulation process transitioning from atomized droplets to solid particles.The water evaporation rate from the droplets dictated the ultimate size and shape of the resultant particles.Given its hygroscopic nature as a salt filler, LiCl extended the evaporation duration of the water within the droplets during spray drying, resulting in enlarged particle dimensions.At excessive LiCl ratios (26%), incomplete drying of the particle exteriors could occur, resulting in interparticle adhesion.Moreover,  www.nature.com/scientificreports/superabundant LiCl modified the surface tension of the aqueous solution, diminishing the capillary forces that acted upon the particle exteriors and compromising their sphericity.Moreover, higher LiCl concentrations precipitated on the particle surfaces, influencing the morphological integrity of the composite particles during the drying phase.As shown in Fig. 2, the LiCl-LDHs composite microspheres containing a minimal LiCl fraction (2%) exhibited smooth exteriors with an absence of discernible LiCl precipitates, which was indicative of the intraspherical distribution of lithium salts 23 .Increasing LiCl ratios resulted in an incremental roughening of the composite microsphere surfaces, which was particularly noticeable at an 18% LiCl-LDHs concentration.At a critical threshold of 26% LiCl, the microsphere surfaces were noticeably enriched with LiCl particulates.Concurrently, the composite particles displayed an uneven morphology, with a significantly increased tendency for agglomeration 24 .
Figure 3 presents the particle size distribution and specific surface area measurements of the LiCl-LDHs composite microspheres.Particle sizes resulting from spray granulation ranged from 10 to 90 μm, demonstrating a wide distribution.The particle size distributions of the samples showed minor variations in response to different LiCl concentrations.Analysis of the median particle size (D 50 ) data, as illustrated in Fig. 3b, suggested that LiCl incorporation decreased the water evaporation rate in spray drying, resulting in a slight increase in microsphere size with higher LiCl levels.At an 18% LiCl concentration, the median particle size (D 50 ) of the sample increased to 26.9 μm.However, further increases in LiCl content led to a significant reduction in particle size, which could be attributed to the compromised spherical morphology.
The internal architecture of the composite microspheres was also examined using specific surface area analyses.Figure 3c demonstrates a significant decrease in the specific surface area of the composite microspheres as the LiCl content increased, particularly at higher concentrations.When correlated with the SEM images and particle size distribution data, it was clear that variances in external size and morphology were minor across the range of 2-18% LiCl content.Consequently, the substantial difference observed in the specific surface area suggested that changes occurred within the internal structures of the microspheres.These findings indicated a considerable effect of LiCl incorporation on the inner structure of the composite microspheres.
Building on established research 25 , this study confirmed that the Mg-Al layered hydroxide materials, synthesized via co-precipitation, consisted of nanoparticle flakes.This morphology resulted in the formation of numerous internal voids during the subsequent spray drying stages.The data presented in Fig. 3d indicate a trend of both the average pore size and porosity of the composite microspheres gradually decreasing with increasing LiCl content.This trend likely originated from the precipitation of lithium salts during the drying phase, which occupied the voids within the microspheres 26 .Specifically, at a lower LiCl threshold (≤ 10%), the microspheres maintained high porosity levels (> 0.39 cm 3 /g) with pore sizes exceeding 35 nm.Conversely, at an LiCl concentration of 26%, an excess of lithium salt resulted in nearly closed internal pores, thus reducing the porosity to 0.016 cm 3 /g and decreasing the pore diameter to approximately 11.98 nm.
The FT-IR spectra of the LiCl-LDHs composite microspheres, recorded over a 400-4000 cm −1 range, are illustrated in Fig. 4. The peak approximately at 3455 cm −1 was attributed to the O-H stretching vibrations, suggesting the presence of surface-adsorbed and interlayer water within the samples 27 .The broadening phenomenon of this peak, correlated with an increase in LiCl content, indicated an enhanced water retention capacity that was attributable to the hygroscopic nature of LiCl.A peak emerged at 1637 cm −1 due to the bending vibrations of crystalline water 28 .The band at 1500 cm −1 possibly resulted from interactions between OH − ions and Li +29 .Moreover, the distinct peak proximate to 1359 cm −1 could be attributed to the C-O stretching vibrations, which indicated the intercalation of CO 3 2− in the LDH layers, consisting of a byproduct of atmospheric CO 2 exposure during sample handling 30 .Upon addition of LiCl, the vibrational peak at 1359 cm −1 disappears and transforms into a small shoulder at 1400 cm −1 , indicating a decrease in the symmetry of the carbonate anion.This is most likely due to some interaction between the free carbonate anion and its surroundings 31 .The spectral region ranging from 500 to 790 cm −1 included the translational and deformation modes of Al-OH bonds, and the band observed near 445 cm −1 corresponded to the O-M-O (where M = Mg or Al) lattice vibrations within the octahedral layers of Mg-Al LDHs 32 .The maintenance of these signature infrared features across the spectrum confirmed that the core chemical structure of the Mg-Al LDHs material remained intact despite the incorporation of LiCl.
To clarify the influence of LiCl content on the moisture uptake efficacy of Mg-Al LDHs, the hygroscopic profiles of different LiCl-LDHs composite microspheres were assessed under conditions of constant temperature and elevated humidity.As shown in Fig. 5a, a direct correlation was evident between the LiCl proportion in the composite and its corresponding water-loading capacity.Significantly, the sample without LiCl exhibited the lowest saturation moisture uptake ratio, registering only 0.32 g/g.The homogeneous distribution of LiCl, even in modest amounts, in the microsphere pores notably enhanced the moisture absorption capacity of the composite material, thus simultaneously improving the water-loading capacity of the internal micro-pores and interfaces.During the initial hygroscopic stage, adsorbed water was present in the form of solid crystalline hydrates.With increasing water content, a saline solution progressively formed and permeated the internal pores of the microspheres, endowing the material with the ability to chemically absorb moisture 33 .According to this hygroscopic mechanism, the greater the LiCl content in the composite microsphere, the more pronounced its hygroscopic ability.However, with the inclusion of 26% LiCl, the maximum saturation moisture uptake ratio reached 3.4 g/g.Nevertheless, the absorbed water was not limited to the internal pores of the microspheres but also formed a thin film on the surface of the particles, indicating a deliquescence phenomenon, which led to powder agglomeration.
To examine the effect of LiCl content on the optical properties of the composite microspheres in greater detail, the visible and near-infrared reflectance spectra of the LiCl-LDHs composite microspheres before and after moisture absorption were analyzed.Figure 5b shows the visible and near-infrared spectral curves of the LiCl-LDHs samples in a desiccated state.Although the pure Mg-Al LDHs microspheres displayed spectral characteristics analogous to green leaves, the overall spectral reflectance was substantially higher than that of natural foliage.Moreover, the water absorption peak intensity of the desiccated microspheres was noticeably subdued, indicating significantly lower water content relative to natural plants.When a minimal quantity of LiCl (≤ 10%) was introduced to the microspheres, the spectral shape of the desiccated samples was largely retained.However, due to the high reflectance of LiCl, the spectral reflectance of the composite microspheres experienced a minor elevation.With increasing LiCl concentrations (≥ 18%), the position of the red edge was found to gradually shift toward longer wavelengths, spanning from 630 to 750 nm.This shift likely resulted from the precipitation of LiCl particles onto the surfaces of the microspheres with elevated LiCl content, resulting in a light scattering effect that intensified light absorption in the 700-760 nm range.Furthermore, an enhanced water www.nature.com/scientificreports/peak intensity in the near-infrared band was indicative of the tendency of the microspheres to absorb moisture from the surrounding air. Figure 5c presents the spectral curves of the LiCl-LDHs composite microspheres following complete moisture absorption.Each sample was saturated with moisture after 74 h.For LDHs samples without LiCl, the spectral shape and reflectance exhibited negligible variations due to weak hygroscopicity.By contrast, incorporating LiCl into the LDHs materials resulted in increased water content, which altered the material's refractive index and markedly reduced the spectral reflectance across the entire visible and near-infrared band.Using the sample with 2% LiCl content as an example, the average spectral reflectance at 400-2500 nm was found to decrease from 66 to 58% after hygroscopic absorption.With increasing LiCl content, the water content in the sample also increased, leading to a further reduction in spectral reflectance.Notably, the red edge position of the sample experienced only a 20 nm redshift following hygroscopic absorption, and the spectral shape became more akin to that of a green leaf.Specifically, the near-infrared reflectance of the sample was slightly lower than that of natural plants, which was attributed to the increased water content in the sample after hygroscopic absorption.The absorbed water dissolved some of LiCl, diminishing its influence on spectral characteristics.However, water also modified the refractive index of the composite particles to a degree, thus enhancing the scattering and absorption of incident light.Ultimately, the visible light spectra of the composite microsphere samples closely matched that of plant leaves, while the reflectance of the near-infrared spectrum remained noticeably lower than that of plant leaves.
To facilitate the visual comparison of the intensity variations among characteristic absorption peaks, the reflectance spectral curve of the sample was subjected to envelope removal.As shown in Fig. 5d, at lower LiCl concentrations, the intensity of the water absorption peaks near 1450 and 1940 nm correlated with the concentration of LiCl.The water peak intensities for the 10% and 18% LiCl-LDHs composite microspheres were found to be relatively high.However, with further increases in LiCl content, the intensities of the water absorption peaks diminished.This phenomenon could be attributed to excess lithium salt, which caused a significant amount of brine solution to form not only within the microporous material but also on the surface of the powder 34 .However, to prevent instrument contamination during spectral testing, the removal of water on the coating surface was imperative.As a result, the water content indicated by the spectral test results was substantially lower than the www.nature.com/scientificreports/actual water content in the sample.Along with the analysis of the microsphere morphology and structure, the comprehensive performance of the 10% LiCl-LDHs samples proved to be superior, demonstrating the closest resemblance to the visible and near-infrared spectra of natural plants.At this point, the spectral similarity index, r xy , achieved a value of 95.58%.Subsequently, coating samples were fabricated utilizing x% LiCl-LDHs microsphere pigments, and their hygroscopic curves and reflectance spectra were evaluated.As illustrated in Fig. 6a, the coating fabricated with a 2% LiCl-LDHs pigment exhibited a saturation moisture uptake ratio of 0.34 g/g.Compared with the coating without LiCl (0.26 g/g), the moisture uptake was marginally enhanced.The coating sample incorporating 10% LiCl-LDHs pigment demonstrated the highest moisture uptake capability, with a maximum saturation moisture uptake ratio of 0.75 g/g.With further increases in LiCl content, the moisture uptake capacity of the coating diminished.The saturation moisture uptake ratio for the coating with 26% LiCl-LDHs was only 0.18 g/g.The water absorption ratio of the coating was noticeably lower than that of the LiCl-LDHs powder because the composite microsphere particles were uniformly embedded in the resin, and their surfaces were entirely encased by acrylic resin.The microsphere particles could only interact with atmospheric moisture via confined pathways, thus significantly constraining the hygroscopic process.
When the coating encompassed an optimal amount of LiCl, water could permeate the coating through the pores and could be subsequently absorbed by the composite microspheres and retained within their structure.However, when the LiCl concentration exceeded a certain threshold, an excessive quantity of lithium salt became intermixed with the LDHs material and could also coat the surface of the microspheres.Upon water absorption, the lithium salt progressively dissolved, and excess salt solution could not be sustained at the powder-resin interface, necessitating its migration toward the coating surface through the pores.Throughout this process, the significant depletion of lithium salt diminished the effective LiCl concentration in the coating, consequently leading to a reduction in its water absorption capacity.In addition, the migration of LiCl may also block the internal channels of atmospheric moisture into the coating, thereby reducing the water absorption capacity of composite particles and pores.The relevant influence mechanisms are shown in Fig. 7.As indicated by the spectral curve in Fig. 6, the influence of LiCl on the spectral properties of the dry coating was the same as that the composite particles.With an increase in LiCl content, a gradual reduction in spectral reflectance was observed, accompanied by a pronounced redshift in the spectral characteristics of the red edge.All the coated samples were subjected to moisture absorption for 24 h and all the samples were saturated with moisture absorption rate.After subjecting the coating material to saturated moisture absorption, the spectral reflectance diminished further, aligning with the change in spectral curve with the water absorption characteristics.As illustrated in Fig. 6d, when the LiCl concentration in the coating was 10%, the peak of spectral water absorption was most pronounced, and the spectral profile more closely resembled that of natural vegetation, with a spectral curve similarity reaching an impressive value of 97.41%.
To determine the cyclic hygroscopicity of the composite coating, a series of 10 drying and moisture absorption cycles was performed on the 10% LiCl-LDHs coating samples.Figure 8a presents the mass fluctuation curve of the sample following repeated drying and hygroscopic cycle treatment.Despite observed fluctuations in the mass of the coating, it retained a relatively consistent moisture absorption capacity, and the water absorption ratio was generally sustained at approximately 0.77 g/g.As indicated by the spectral curve in Fig. 8b, repeated drying and moisture absorption treatment did not significantly change the visible-near-infrared reflectance spectrum of the coating.The spectral congruence between the samples and natural vegetation remained at approximately 95%.This suggested that the composite material exhibited robust resilience to drastic changes in ambient temperature and humidity, demonstrating considerable environmental adaptability.
Finally, the camouflage efficacy of the coatings in the context of hyperspectral imaging was illustrated, as shown in Fig. 9. Attempts were made to detect the coatings positioned against a foliar background employing a  hyperspectral camera.Figure 9c shows the near-infrared spectral curves (900-2500 nm) derived from the hyperspectral image.Analysis revealed that the near-infrared spectrum of the 10% LiCl-LDH coatings demonstrated the closest resemblance to that of natural vegetation in terms of both spectral shape and intensity.
To advance the verification of the spectral discrepancy effects on near-infrared hyperspectral camouflage, spectral angle mapping (SAM) and Mahalanobis distance (MD) mapping classifications were employed to assess the similarity between the coatings and the plant backdrop.SAM constituted a physically grounded spectral classification method that used an n-dimensional angle for aligning pixels with the reference spectra 35 .By setting a cosine similarity threshold, precise mapping of the areas with a higher cosine similarity to the reference spectra could be achieved.This technique focused on discerning the spectral shape disparities between the target and the backdrop within hyperspectral images.In contrast to SAM, MD was characterized by calculating the MD to quantify the disparity between the sample spectrum and background reference spectrum 36 .Through the application of a defined maximum distance threshold, targets with spectral distances exceeding this margin could be distinguished in the hyperspectral images, which primarily captured variances in reflectance between the target and background spectra.
As shown in Fig. 9d, setting the threshold at 96.0% resulted in an accurate classification of most genuine leaves, where all four samples were concurrently mistaken for foliage.An increase in the threshold value decreased the extent of the mask, resulting in a more exact classification.At a threshold of 99%, the 0% LiCl-LDHs, 2% LiCl-LDHs, and 26% LiCl-LDHs samples were effectively differentiated from the mask, thus standing out against the background.Complete isolation of the 10% LiCl-LDHs sample required the threshold to be raised to 99.7%.However, this high threshold introduced an overfitting issue, where a significant number of green leaves were misclassified as false, alongside the 10% LiCl-LDHs sample, thereby rendering this criterion untenable for distinguishing between the camouflage coating and real leaves.
The classification results obtained via the MD are illustrated in Fig. 9e.When the maximum distance error threshold was set to 65, all samples remained indistinguishable against the background.Due to the most pronounced spectral reflectance difference between the 0% LiCl-LDHs sample and natural leaves, the former was partially detectable at a maximum distance error of 55, while the latter three samples continued to be classified as plant leaves.After reducing the maximum distance error to 45, the 2% LiCl-LDHs and 26% LiCl-LDHs samples became distinguishable from the background, while the 10%LiCl-LDHs sample continued to blend with the background.The 10% LiCl-LDHs sample remained undetected against the background until the threshold was further lowered to 35.In summary, the superior hyperspectral camouflage capabilities of the 10% LiCl-LDHs coating were corroborated in practical scenarios.Unlike traditional optical camouflage materials, which may be readily detectable, an optimal concentration of LiCl enhanced the water content of the coating, which contributed to the augmented scattering and absorption effects of near-infrared light.The intensity and shape of the spectrum more closely resembled those of natural leaves, indicating significant potential for application in hyperspectral camouflage.

Conclusion
Artificial camouflage materials inspired by natural camouflage mechanisms have evolved in response to the demands of military technology.Recent advancements in spectral imaging technology for target detection have driven the evolution of camouflage technology toward greater dimensionality and precision.To effectively conceal military targets against a background, the VIS and NIR spectral properties of camouflage materials must be precisely tailored to mimic their surroundings with high fidelity.
In this work, the LiCl-LDHs composite microspheres were synthesized using a spray granulation technique and served as a functional pigment in the hyperspectral camouflage coatings, achieving the accurate simulation and control over the visible to near-infrared spectral trait characteristics of green foliage.After the spray granulation process, the LiCl-LDHs powder displayed spherical particles with smooth surfaces, and LiCl was primarily localized in the internal cavities of the Mg-Al LDHs microspheres.LiCl significantly enhanced the hygroscopic properties of the composite microspheres, which were positively correlated with the LiCl content.However, an excessive concentration of LiCl could extend the spray drying process, potentially compromising the crystalline structure and particle morphology of the Mg-Al LDHs microspheres.The results indicated that the camouflage coating containing 10% LiCl-LDHs composite microspheres demonstrated the highest water absorption capacity.When compared with coatings lacking LiCl, the water absorption ratio could be increased from 0.26 to 0.75 g/g.This composite microsphere material featured the individual tunability of red edge and NIR reflectance, which mimicked the spectral variation of natural leaves in the realistic canopy.The spectral match between the coating and natural foliage could reach 97.41%, suggesting significant potential for hyperspectral camouflage applications across the VIS to NIR spectra.Additionally, the coating demonstrated good environmental adaptability, preserving its VIS and NIR spectral properties even after undergoing 10 cycles of drying and moisture absorption testing.
Ultimately, the LiCl-LDHs composite microspheres endowed the artificial coating with robust camouflage capabilities against hyperspectral target detection, which could be mistaken for foliage by the SAM and MD mappers to an overfitting level.This novel material design approach may provide a new method for the development of high-performance hyperspectral camouflage materials.

Figure 3 .
Figure 3. Particle size distribution (a), D50 particle size (b), specific surface area (c) and average pore size (d) of LiCl-LDHS composite microspheres with different LiCl content.

Figure 5 .
Figure 5. Water absorption ratio curves and spectral curves of LiCl-LDHs composite microsphere with different LiCl content [(a) hygroscopic curves; (b) spectral curves of dry powders; (c) spectral curves after saturation moisture absorption; (d) continuum removal spectrum after saturation moisture absorption].

Figure 6 .
Figure 6.Water absorption ratio curves and spectral curves of composite coating with different LiCl content [(a) hygroscopic curves; (b) spectral curves of dry coating; (c) spectral curves after saturation moisture absorption; (d) continuum removal spectrum after saturation moisture absorption].

Figure 8 .
Figure 8. Mass change data (a) and reflection spectral curves (b) of 10% LiCl-LDHs composite coating after n times of drying and moisture absorption cycle experiment.

Figure 9 .
Figure 9. Concealment of LiCl-LDHs coatings in the hyperspectral image [(a) the optical images of LiCl-LDHs powders and coatings; (b) the optical images of LiCl-LDHs coatings in the leaf background; (c) NIR spectral curves extracted from the hyperspectral image; (d) SAM classification results of camouflage coatings in leaf background with different thresholds; (e) MD classification results of camouflage coatings in leaf background with different threshold].